N08811 Chemical composition:
Alloy |
% |
Ni |
Cr |
Fe |
C |
Mn |
Si |
Cu |
S |
Al |
Ti |
800HT |
Min. |
30 |
19 |
balance |
0.05 |
|
|
|
|
0.15 |
0.15 |
Max. |
35 |
23 |
0.10 |
1.5 |
1 |
0.75 |
0.015 |
0.60 |
0.60 |
N08811 Physical properties:
Density |
8.0 g/cm³ |
Melting point |
1350-1400ºC |
N08811 Alloy m inimum mechanical properties in the room temperature
Alloy |
Tensile strength Rm
N/mm² |
Yield strength RP0. 2
N/mm² |
Elongation A5
% |
800H |
500 |
210 |
35 |
N08811 Characteristic as below:
1.Excellent corrosion resistance in the high temperature at 500ºC in the water medium.
2.Good stress corrosion resistance property.
3.Excellent machining
N08811 Metallurgical structure:
800H is face-centered cubic lattice structure. very low carbon centent and increased Ti:C rate
improve the stability of the structure, anti-allergy , and anti-intergranular corrosion. Low temperature annealing of 950ºC ensure the fine grain structure.
N08811 Corrosion resistance:
800H can not be corroded in many kinds of media. Its high nickel content made it have good stress corrosion resistance cracking property in the water corrosion condition.High Chromium content made it can better resist pitting and crevice corrosion cracking. This alloy can resist nitric acid and organic acid corrosion, but it is not so fine in the sulfuric acid and hydrochloric acid.
800H not only good corrosion resistance in both oxidation and non-oxidizing salt, maybe a little pitting in halide, but also very good corrosion resistance property in the mixture of water,smoke, steam,air and carbon dioxide.
N08811 Application range and field:
1.Nitrate condenser---Corrosion resistance of nitrc acid
2.Steam heating pipes--Very good mechanical property
3.Heat up element tube--Very good mechanical property
For the application of up to 500ºC enviornment, alloy supply state change to annealing.